DESCRIPTION: N3510 is a blend of reinforcing materials with nitrile
latex, produced by the wet process. N3510 offers excellent torque
retention, resistance to crush extrusion and sealability. N3510
is recommended for use in solid core head gasket applications. Because
of its strong thermal properties and sealability, N-3510 is also
recommended for use in high temperature soft gasket and exhaust
gasket applications.
|
RECOMMENDED APPLICATION:
|
ALL SEALING APPLICATIONS: Soft Gasket,
Exhaust Applications, Solid Core / Perforated Core Cyl. Head
Gaskets
|
|
TEMPERATURE RATING: - FLUID SEALING
|
570° F
|
300° C
|
|
TEMPERATURE RATING: - EXHAUST
|
1150° F
|
621° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .020" / .022" / .032"
|
.4mm / .5mm / .55mm / 8mm
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES **
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft. cu.
|
81
|
ASTM F-104
|
density g/cm cu.
|
1.30
|
|
tensile psi
|
1367
|
ASTM F-152
|
tensile MPa
|
9.4
|
|
Compression @ 5000 psi
|
20%
|
ASTM F-36
|
Compression @ 34.5 MPa
|
20%
|
|
recovery
|
47%
|
ASTM F-36
|
recovery
|
47%
|
|
IGNITION LOSS,
1 Hr. @ 1500° F
|
27.7%
|
ASTM G-495
|
IGNITION LOSS,
1 Hr. @ 815° C
|
27.7%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
ASTM OIL # 3,
5 hours @ 300° F
|
|
ASTM F-146
|
ASTM OIL # 3,
5 hours @ 150° C
|
|
|
weight increase
|
30%
|
|
weight increase
|
30%
|
|
thickness increase
|
3%
|
|
thickness increase
|
3%
|
|
COOLANT,
5 hours @ 180° F
|
|
ASTM F-146
|
COOLANT,
5 hours @ 82° C
|
|
|
weight increase
|
41.7%
|
|
weight increase
|
41.7%
|
|
thickness increase
|
8.2%
|
|
thickness increase
|
8.2%
|
|
sealability
|
|
ASTM F-37
|
sealability
|
|
|
ASTM fuel a,
500 psi 30 in HG, cc/hr
|
7.7
|
|
ASTM fuel a,
3.5 MPa 762mm Hg, cc/hr.
|
7.7
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.