DESCRIPTION: N5000 composite material is a blend of aramid reinforcing
materials and nitrile latex, produced by the wet process, which
yields a homogeneous gasketing material. N5000 offers excellent
thermal properties, sealability and fire ring support.
|
RECOMMENDED APPLICATION:
|
Cylinder Head Gasket - Solid Core
|
|
TEMPERATURE RATING:
|
750° F
|
400° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .028" / .032"
|
.4mm / .7mm / .8mm
|
| PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES ** |
TEST METHOD |
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES |
| density lbs./ ft.cu. |
81 |
ASTM F-104 |
density g/cm cu. |
1.29 |
| tensile psi |
1630 |
ASTM F-152 |
tensile MPa |
11.2 |
| Compression @ 5000 psi |
21% |
ASTM F-36 |
Compression @ 34.5 MPa |
21% |
| recovery |
51% |
ASTM F-36 |
recovery |
51% |
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
ASTM Fuel b,
5 hours @ 73° F
|
|
ASTM F-146
|
ASTM FuelB,
5 hours @ 23° C
|
|
|
weight increase
|
39%
|
|
weight increase
|
39%
|
|
ASTM OIL # 3,
5 hours @ 300° F
|
|
ASTM F-146
|
ASTM OIL # 3,
5 hours @ 150° C
|
|
|
weight increase
|
33%
|
|
weight increase
|
33%
|
|
thickness increase
|
4%
|
|
thickness increase
|
4%
|
|
sealability
|
|
ASTM F-37
|
sealability
|
|
|
Coolant
500 psi ext./60 psi int. ml/hr
|
.071
|
|
Coolant
3.5 MPa /.41Mpa int. ml/hr.
|
.071
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
* PRELIMINARY SPECIFICATIONS MAY VARY SLIGHTLY FROM NORMAL PRODUCTION
VALUES.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.