DESCRIPTION: MAGNASEAL™ - N6125 is a blend of aramid fiber
and nitrile latex, produced by the wet process, yielding a homogeneous
gasketing material in a 0.125" caliper. N6125 is intended for
use in general soft gasket applications up to 265° F.
|
RECOMMENDED APPLICATION:
|
General Purpose Soft Gasket
|
|
TEMPERATURE RATING:
|
265° F
|
137° C
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft. cu.
|
75
|
ASTM F-104
|
density g/cm cu.
|
1.20
|
|
tensile psi
|
1000
|
ASTM F-152
|
tensile MPa
|
6.9
|
|
Compression @ 5000 psi
|
22%
|
ASTM F-36
|
Compression @ 34.5 MPa
|
22%
|
|
recovery
|
40%
|
ASTM F-36
|
recovery
|
40%
|
|
Creep Relaxation
@ 212° F / 3000 psi
|
57%
|
ASTM F-38
|
Creep Relaxation
@ 100° C / 20.7 MPa
|
57%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
IRM oil 903,
5 hours @ 300° F
|
|
ASTM F-146
|
IRM oil 903,
5 hours @150° C
|
|
|
weight increase
|
35%
|
|
weight increase
|
35%
|
|
thickness increase
|
5%
|
|
thickness increase
|
5%
|
|
Ethylene Glycol / Water
5 hours @ 180° F
|
|
ASTM F-146
|
Ethylene Glycol / Water
5 hours @ 82° C
|
|
|
weight increase
|
35%
|
|
weight increase
|
35%
|
|
thickness increase
|
2%
|
|
thickness increase
|
2%
|
|
ASTM Fuel b
RT for 5 hr.
|
|
ASTM F-37
|
ASTM Fuel b
RT for 5 hr.
|
|
|
weight increase
|
27%
|
|
weight increase
|
27%
|
|
thickness increase
|
5%
|
|
thickness increase
|
5%
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
* PRELIMINARY SPECIFICATIONS MAY VARY FROM NORMAL PRODUCTION VALUES.