DESCRIPTION: MAGNASEAL™ N6500V is a blend of aramid fiber and
nitrile latex, produced by the wet process, yielding a homogeneous
gasketing material accross a wide range of thicknesses. N6500V is
intended for use in Heavy Duty and Industrial Applications where
the gasket is exposed to high temperatures, loads and shear forces.
N6500V features our proprietary "VFS" quick-release coating
which will also accept printing or beading.
|
RECOMMENDED APPLICATION:
|
Heavy Duty/Industrial Applications
|
|
TEMPERATURE RATING:
|
650° F
|
350° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .032" / .062" / .090"
|
.4mm / .8mm / 1.6mm / 2.3mm
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES **
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft. cu.
|
105
|
ASTM F-104
|
density g/cm cu.
|
1.68
|
|
tensile psi
|
2500
|
ASTM F-152
|
tensile MPa
|
17.2
|
|
Compression @ 5000 psi
|
14%
|
ASTM F-36
|
Compression @ 34.5 MPa
|
14%
|
|
recovery
|
70%
|
ASTM F-36
|
recovery
|
70%
|
|
creep relaxation
@ 300° F / 3000 psi
|
27%
|
ASTM F-38
|
creep relaxation
@ 150° C / 20.7 MPa
|
27%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
IRM oil 903,
5 hours @ 300° F
|
|
ASTM F-146
|
IRM oil 903,
5 hours @150° C
|
|
|
weight increase
|
14%
|
|
weight increase
|
14%
|
|
thickness increase
|
2%
|
|
thickness increase
|
2%
|
|
ethylene glycol / water
5 hours @ 180° F
|
|
ASTM F-146
|
ethylene glycol / water
5 hours @ 82° C
|
|
|
weight increase
|
20%
|
|
weight increase
|
20%
|
|
thickness increase
|
4%
|
|
thickness increase
|
4%
|
|
sealability
|
|
ASTM F-37
|
sealability
|
|
|
ASTM Fuel a,
500 psi / 30 in Hg, ml/hr.
|
3
|
|
ASTM Fuel a,
3.45 MPa / 762mm Hg, ml/hr.
|
3
|
|
Nitrogen Seal
@ 3000 psi / 30 psi cc / min.
|
.6
|
|
Nitrogen Seal
@ 20.7 Mpa / .21 Mpa cc/ min.
|
.6
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.