DESCRIPTION: MAGNASEAL™ - S6200V is a blend of aramid fiber
and SBR latex, produced by the wet process, yielding a homogeneous
gasketing material across a wide range of thicknesses. S6200V is
intended for Heavy Duty Applications where the gasket is exposed
to high temperatures, loads and shear forces. S6200V features our
proprietary "VFS" quick-release coating which will accept
printing or beading.
|
RECOMMENDED APPLICATION:
|
Heavy Duty Sealing
|
|
TEMPERATURE RATING:
|
700° F
|
370° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .032" / .047" / .062"
|
.4mm / .8mm / 1.2mm / 1.6mm
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES **
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft. cu.
|
83
|
ASTM F-104
|
density g/cm cu.
|
1.33
|
|
tensile psi
|
2040
|
ASTM F-152
|
tensile MPa
|
14.1
|
|
Compression @ 5000 psi
|
15%
|
ASTM F-36
|
Compression @ 34.5 MPa
|
15%
|
|
recovery
|
50%
|
ASTM F-36
|
recovery
|
50%
|
|
creep relaxation
@ 400° F / 3000 psi
|
32%
|
ASTM F-38
|
creep relaxation
@ 205° C / 20.7 MPa
|
32%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
IRM oil 903,
5 hours @ 300° F
|
|
ASTM F-146
|
IRM oil 903,
5 hours @150° C
|
|
|
weight increase
|
45%
|
|
weight increase
|
45%
|
|
thickness increase
|
43%
|
|
thickness increase
|
43%
|
|
ethylene glycol / water
5 hours @ 180° F
|
|
ASTM F-146
|
ethylene glycol / water
5 hours @ 82° C
|
|
|
weight increase
|
31%
|
|
weight increase
|
31%
|
|
thickness increase
|
12%
|
|
thickness increase
|
12%
|
|
sealability
|
|
ASTM F-37
|
sealability
|
|
|
ASTM Fuel a,
400 psi / 20 in Hg, ml/hr.
|
.7
|
|
ASTM Fuel a,
2.75 MPa / 508mm Hg, ml/hr.
|
.7
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.
top
|