DESCRIPTION: MAGNASEAL™ - S6600 is a blend of aramid fiber
and SBR latex, produced by the wet process, yielding a homogeneous
gasketing material accross a wide range of thicknesses S6600 is
intended for use in heavy duty and industrial applications.
|
RECOMMENDED APPLICATION:
|
Heavy Duty / Industrial Sealing
|
|
TEMPERATURE RATING:
|
650° F
|
350° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .032" / .062" / .090"
|
.4mm / .8mm / 1.6mm / 2.3mm
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES**
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft. cu.
|
100
|
ASTM F-104
|
density g/cm cu.
|
1.60
|
|
tensile psi
|
2000
|
ASTM F-152
|
tensile MPa
|
13.8
|
|
Compression @ 5000 psi
|
16.5%
|
ASTM F-36
|
Compression @ 34.5 MPa
|
16.5%
|
|
recovery
|
67%
|
ASTM F-36
|
recovery
|
67%
|
|
Creep Relaxation
@ 300° F / 3000 psi
|
34%
|
ASTM F-38
|
Creep Relaxation
@ 150° C / 20.7 MPa
|
34%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
IRM oil 903,
5 hours @ 300° F
|
|
ASTM F-146
|
IRM oil 903,
5 hours @150° C
|
|
|
weight increase
|
31%
|
|
weight increase
|
31%
|
|
thickness increase
|
23%
|
|
thickness increase
|
23%
|
|
Ethylene Glycol / Water
5 hours @ 180° F
|
|
ASTM F-146
|
Ethylene Glycol / Water
5 hours @ 82° C
|
|
|
weight increase
|
25%
|
|
weight increase
|
25%
|
|
thickness increase
|
4.8%
|
|
thickness increase
|
4.8%
|
|
Sealability
|
|
ASTM F-37
|
Sealability
|
|
|
ASTM Fuel a,
500 psi / 30 in Hg, ml/hr.
|
1.86
|
|
ASTM Fuel a,
3.45 MPa / 762mm Hg, ml/hr.
|
1.86
|
|
Nitrogen Seal
@ 3000 psi / 30 psi cc / min.
|
.86
|
|
Nitrogen Seal
@ 20.7 Mpa / .21 Mpa cc/ min.
|
.86
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.