DESCRIPTION: N2100 is a blend of reinforcing materials and nitrile
latex, produced by the wet process, which yields a homogeneous gasketing
material. N2100 is recommended for general purpose high temperature
soft gasket applications.
|
RECOMMENDED APPLICATION:
|
High Temp.Soft Gasket Applications
|
|
TEMPERATURE RATING:
|
550° F
|
285° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.023" / .0275" / .032" / .035"
|
.6mm / .7mm / .8mm /.9mm
|
|
FLUID IMMERSIONS
|
TYPICAL
VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
ASTM FUEL B,
22 hours @ 73° F
|
|
ASTM F-146
|
ASTM FUEL B,
22 hours @ 23° C
|
|
|
weight increase
|
33%
|
|
weight increase
|
33%
|
|
thickness increase
|
2.5%
|
|
thickness increase
|
2.5%
|
|
ASTM OIL # 3,
5 hours @ 300° F
|
|
ASTM F-146
|
ASTM OIL # 3,
5 hours @ 150° C
|
|
|
weight increase
|
44%
|
|
weight increase
|
44%
|
|
thickness increase
|
1.5%
|
|
thickness increase
|
1.5%
|
|
COOLANT,
5 hours @ 180° F
|
|
ASTM F-146
|
COOLANT,
5 hours @ 82° C
|
|
|
weight increase
|
55%
|
|
weight increase
|
55%
|
|
thickness increase
|
4.5%
|
|
thickness increase
|
4.5%
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
* PRELIMINARY SPECIFICATIONS MAY VARY SLIGHTLY FROM NORMAL PRODUCTION
VALUES.
** NOTE: Typical Values are based upon .032" (.8mm) caliper
material.