DESCRIPTION: N2300 is a blend of reinforcing materials and nitrile
latex, produced by the wet process, which yields a homogeneous gasketing
material. N2300 is recommended for general purpose soft gasket applications.
|
RECOMMENDED APPLICATION:
|
High Temp. Soft Gasket Applications
|
|
TEMPERATURE RATING:
|
500° F
|
260° C
|
|
AVAILABLE CALIPERS (in.) & (mm)
|
.016" / .032" / .045" / .062"
|
.4mm / .8mm / 1.2mm / 1.6mm
|
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES **
|
TEST METHOD
|
PHYSICAL TEST ORIGINAL PROPERTIES
|
TYPICAL VALUES
|
|
density lbs./ ft.cu.
|
60
|
ASTM F-104
|
density g/cm cu.
|
.96
|
|
tensile psi
|
> 600
|
ASTM F-152
|
tensile MPa
|
> 4.13
|
|
Compression @ 1000 psi
|
27%
|
ASTM F-36
|
Compression @ 6.9 MPa
|
27%
|
|
recovery (min)
|
30%
|
ASTM F-36
|
recovery (min)
|
30%
|
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
TEST METHOD
|
FLUID IMMERSIONS
|
TYPICAL VALUES
|
|
ASTM FUEL B,
22 hours @ 73° F
|
|
ASTM F-146
|
ASTM FUEL B,
22 hours @ 23° C
|
|
|
weight increase
|
35%
|
|
weight increase
|
35%
|
|
thickness increase
|
2%
|
|
thickness increase
|
2%
|
|
ASTM OIL # 3,
5 hours @ 300° F
|
|
ASTM F-146
|
ASTM OIL # 3,
5 hours @ 150° C
|
|
|
weight increase
|
44%
|
|
weight increase
|
44%
|
|
thickness increase
|
2%
|
|
thickness increase
|
2%
|
|
COOLANT,
5 hours @ 180° F
|
|
ASTM F-146
|
COOLANT,
5 hours @ 82° C
|
|
|
weight increase
|
56%
|
|
weight increase
|
56%
|
|
thickness increase
|
6%
|
|
thickness increase
|
6%
|
The performance data contained herein are based on laboratory tests
and represent typical values. This technical data sheet is not intended
to be used as a purchase specification. The information contained
in this document is proprietary and may NOT be reproduced in any
form without the written permission of HOLLINGSWORTH & VOSE
Company.
* PRELIMINARY SPECIFICATIONS MAY VARY SLIGHTLY FROM NORMAL PRODUCTION
VALUES.
** NOTE: Typical Values are based upon .032" (.8mm) caliper